本研究以實驗方式利用斜板式與狹縫式模具的組合(S-X組合)針對聚乙烯醇(polyvinyl alcohol, PVA)水溶液進行預調式雙層塗佈實驗。研究主要在比較S-X雙層模具與外部接觸型雙層共擠壓式塗佈，實驗發現S-X模具雙層塗佈較外部接觸型雙層共擠壓式更有利於低黏度、低流量比的操作條件，且適用於上下層黏度比範圍大的情形，只要實驗流體能夠在S-X模具上的斜板成膜，即可進行雙層塗佈，並不會出現外部接觸型雙層塗佈在流量比低時因上層塗液膜厚過低而產生的spreading failure現象。在塗佈缺陷方面，低塗佈速率下出現之缺陷為下層所主導的空氣滲入現象；在高塗佈速率下則容易受到上層流體不穩定的影響而產生橫向波塗佈缺陷，此種塗佈缺陷與外部接觸型雙層塗佈相當類似。
利用S-X模具進行雙層塗佈所得到的上層液膜厚度可以達到5μm以下甚至更薄，相較於以往的塗佈方式可以獲得超薄的塗層。添加少量高分子如CMC有助於增大塗佈視窗以及最大塗佈速率，使得上層液膜可以更薄。
最後利用流場觀察的技術對於雙層塗佈的情形以及塗佈液珠的形狀進行研究，證明由於S-X雙層模具幾何構造的關係使得上層的塗液在進行塗佈操作時能夠較外部接觸雙層共擠壓式更穩定的轉換流動的方向，因此較外部接觸式雙層共擠壓式更有利於低流量比的操作。

Beck, R. H., “Extrusion Apparatus and Processes of Extruding,” U.S. Patent 2,901,770 (1959).

Chino, N., Y. Hiraki, N. Shibata and T. Sato, “Extrusion-type Coating Head for Coating A Magnetic Recording Medium,” U.S. Patent 5,072,688 (1991).

Choinski, E. J. and W. Mass, “Method of Multilayer Coating,” U.S. Patent 4,113,903 (1978).

Cohen, E. B. and E. B. Gutoff, “Modern Coating and Drying Technology,” VCH Press, New York (1992).

Gutoff, E. B. and C. E. Kendrick, “Low Flow Limits of Coating on A Slide Coater,” AIChE J. 33, 141 (1987).

Hens, J. and L. Boiy, “Operation of the Bead of A Premetered Coating Device,” Chem. Eng. Sci. 41, 1827 (1986).

Higgins, B. G. and L. E. Scriven, “Capillary Pressure and Viscous Pressure Drop Set Bounds on Coating Bead Operability,” Chem. Eng. Sci. 35, 673 (1980).

Ishiwata, M, Y. Uchida and Y. Nagai, “Multilayer Coating Method,” U.S. Patent 3,573,965 (1971).

Jackson, B. W., D. E. Winkler and C. B. Woodworth, “Apparatus for coating a multiple number of layers onto a substrate,” US Patent 3,996,885 (1976) .

Lee, K. Y., L. D. Liu and T. J. Liu, “Minimum Wet Thickness in Extrusion Slot Coating,” Chem. Eng. Sci., 47, 1703 (1992).

Miller, F. D., J. J. Wheeler and N. Y. Rochester, “Coating High Viscosity Liquids,” U.S. Patent 3,206,323 (1965).

Ning, C. Y., C. C. Tsai and T. J. Liu, “The Effect of Polymer Additives on Extrusion Slot Coating” Chem. Eng. Sci. 51, 3289 (1996).

Ruschak, K. J., “Limiting Flow in A Pre-metered Coating Device,” Chem. Eng. Sci. 31, 1057 (1976).

Russell, T. A., “Multiple Coating Apparatus,” U.S. Patent 2,761,418 (1956a).

Russell, T. A., “Method of Multiple Coating ” U.S. Patent 2,761,791 (1956b).

Tallmadage, J. A., C.B. Weiberger and H. L. Faust, “Bead Coating Instability：A Comparison of Speed Limit Data with Theory,” AIChE J. 25, 1065 (1979).

俞文正，1994，共擠壓式塗佈技術之建立與分析。國立清華大學化學工程碩士論文。

高明清，1997，高分子添加劑對雙層共擠壓式塗佈的影響。國立清華大學化學工程碩士論文。

林庭瑜，1999，高黏度塗佈視窗之測定與分析。國立清華大學化學工程研究所碩士論文。

林瑜平，1999，PVA水溶液雙層共擠壓式塗佈視窗之研究與分析。國立清華大學化學工程研究所碩士論文。

楊之光，2001，先進狹縫式塗佈研究。國立清華大學化學工程研究所博士論文。