摘要
本研究主要目的在於探討束縛燒結之緻密驅動力。以等溫燒結和非等溫燒結的方式透過兩種不同實驗設施：1.雷射量測系統2. 熱機械分析儀分別取得試片燒結過後之緻密性質、束縛燒結應力與自由燒結驅動力。

實驗結果發現：1.束縛燒結的緻密速率要緩於自由燒結的緻密速率，但不降低緻密程度。2.束縛燒結並無顯著改變自由燒結的燒結控制機制。3.因束縛燒結而所產生的平面張應力數量級足以與X-Y軸向的自由燒結驅動力相抵銷，以致大大減少了整體的平均燒結驅動力，是降低束縛燒結緻密速率的主要因素。4.以非等溫燒結的方式，在升溫速率越慢的燒結條件下，自由燒結與束縛燒結兩者間的燒結緻密曲線差異便越小，且在同溫度下較其他升溫速率快達到燒結緻密。

參考文獻
[1] W.A. Vitrio and R.L. Brown, “Process for Fabricating Dimensionally Stable Interconnect Boards,” US Pat. No. 4, 656, 552, 1987.
[2] K.R. Mikeska and D.T. Schaefer, “Method for Reducing Shrinkage during Firing of Ceramic Bodies,” US Pat. No. 5, 454, 741, 1994.
[3] B. Geller, B. Thaler, A. Fathy, M.J. Liberatore, H.D. Chen, G. Ayers, V. Pendrick and Y. Narayan, “LTCC-M: An Enabling Technology for High Performance Multilayer RF Systems,” J. Microwave, 7, 64-72 (1999).
[4] J. Bang and G. Q. Lu, “Constrained-film Sintering of a Borosilicate Glass：In Situ Measurement of Film Stress,” J. Am. Ceram. Soc., 78 [3] 812-815 (1995)
[5] T.J. Garino and H.K. Bowen, “Deposition and Sintering of Particle Films on a Rigid Substrate,” J. Am. Ceram. Soc., 70 [11] C315-C317 (1987).
[6] T.J. Garino and H.K. Bowen, “Kinetics of Constrained-film Sintering,” J. Am. Ceram. Soc., 73 [2] 251-57 (1990).
[7] E.G. Liniger, R. Raj and D. B. Marshall, “The Instability of Polycrystalline Thin Films: Experiments and Theory,” J. Mater. Res., 5 [1] 151-60 (1990).
[8] G. W. Scherer and T. Garino, “Viscous Sintering on a Rigid Substrate,” J. Am. Ceram. Soc., 68 [4] 216-20 (1985).
[9] A. Jagota and C.Y. Hui, “Mechanics of Sintering Thin Films – I. Formulation and Analytical Results,” Mech. Mater., 9, 107-19 (1990).
[10] A. Jagota and C.Y. Hui, “Mechanics of Sintering Thin Films – II. Cracking due to Self-Stress,” Mech. Mater., 11, 221-34 (1991).
[11] R. K. Bordia and R. Raj, “Sintering Behavior of Ceramic Films Constrained by a Rigid Substrate,” J. Am. Ceram. Soc., 68 [6] 287-92 (1985).
[12] R. K. Bordia and A. Jagota, “Crack Growth and Damage in Constrained Sintering Films,” J. Am. Ceram. Soc., 76 [10] 2475-85 (1993).
[13] T. Cheng and R. Raj, “Flaw Generation During Constrained Sintering of Metal-Glass Multilayer Films,” J. Am. Ceram. Soc., 72 [9] 1649-55 (1989).
[14] M. Ohring, The Material Science of Thin Films(Academic Press, Inc.,San Diego, CA, 1992), pp. 416-418
[15] J. Choe, J.N. Calata, and G.Q Lu, “Constrained-Film Sintering of a gold paste,” J. Mater. Res., 4 [10] 986-994 (1995)
[16] T. Cheng, “Co-Sintering Behavior of Ceramic-Metal and Glass-Metal Multilayer Films:Modeling and Experiment,” Ph.D. Thesis, Cornell University, Ithaca, NY (1989)
[17] 林詠強，簡朝和，”束縛燒結的機制與應力研究，” 國立清華大學材料科學工程學系碩士論文 (2001)
[18] R. K. Bordia and G. W. scherer, “On Constrained Sintering-Ⅰ. Constitutive Model for a Sintering Body,” Acta Metal. 36 [9] 2393-2397 (1988)
[19] G. W. Scherer, “Sintering Inhomogeneous Glasses：Application to Optical Waveguide,” J. Non-cryst. Solid 34, 239 (1979)
[20] P. Z. Cai, G. L. Messing, and D. L. Green, “Determination of the Mechanical Response of Sintering Compacts by Cyclic Loading Dilatometry,” J. Am. Ceram. Soc. 80 [2] 445-52 (1997)
[21] R. K. Bordia and R. Raj, “Sintering Behavior of Ceramic Films Constrained by Rigid Substrate,” J. Am .Ceram. Soc., 68 [6] 287-92 (1985)
[22] V. C. Ducamp and R. Raj, “Shear and Densification of Glass Powder Compacts,” J. Am. Ceram. Soc,. 72 [5] 798-804 (1989)